Título: | Experimental analysis of the carbonation and humidity diffusion processes in aerial lime mortar |
Autor(es): | Oliveira, Mateus António Nogueira Azenha, Miguel Lourenço, Paulo B. Meneghini, A. Guimarães, Erika Tinoco Castro, Fernando Soares, Delfim |
Palavras-chave: | Aerial lime Mortar Carbonation Thermogravimetric analysis Humidity diffusion process Phenolphthalein Compressive strength |
Data: | 2017 |
Editora: | Elsevier |
Revista: | Construction and Building Materials |
Resumo(s): | Aerial lime has been commonly used as binder for preparing mortar in masonry constructions for centuries. Knowledge about the material behaviour of aerial lime is however still limited, and contributions are necessary for better understanding of the evolution of its physical and mechanical properties, in particular concerning the structural behaviour of both historical and new constructions comprising of aerial lime. In this work, an experimental program was developed in order to study aerial lime mortars, specifically addressing the drying and carbonation processes. Regarding the measurement of drying process, the humidity diffusion was monitored in one-dimensional flux conditions. The phenomena associated with self-desiccation were also investigated. For evaluation of the carbonation process, different cylindrical specimens have been studied with phenolphthalein indicator and thermogravimetric analyses. In order to exclusively investigate the carbonation reaction, without the effect of internal humidity gradients in the tested specimens, thin discs of mortar were tested. Also, the compressive strength evolution was analysed using cubic specimens. The most relevant findings can be summarized as following: (i) humidity diffusion was quicker than normally observed in cement-based materials; (ii) a strong effect of the size of specimens has been observed in early ages (before 10 days), which became negligible as time progressed; (iii) up to 70% maximum carbonation was observed in TGA testing, when direct measurement of actual decarboxylation was made, as opposed to mere inference based on the dehydroxylation. |
Tipo: | Artigo |
URI: | https://hdl.handle.net/1822/51529 |
DOI: | 10.1016/j.conbuildmat.2017.04.120 |
ISSN: | 0950-0618 |
e-ISSN: | 1879-0526 |
Versão da editora: | https://doi.org/10.1016/j.conbuildmat.2017.04.120 |
Arbitragem científica: | yes |
Acesso: | Acesso restrito UMinho |
Aparece nas coleções: | ISISE - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
[45].pdf Acesso restrito! | 1,39 MB | Adobe PDF | Ver/Abrir |