Magnetic nanoparticles of zinc/calcium ferrite decorated with silver for photodegradation of dyes

Abstract

Magnetic nanoparticles of zinc/calcium ferrite and decorated with silver were prepared by coprecipitation method. The obtained nanoparticles were characterized by UV/Visible absorption, XRD, TEM and SQUID. The mixed zinc/calcium ferrites exhibit an optical band gap of 1.78 eV. HR-TEM imaging showed rectangular nanoplate shapes with sizes of 10 ± 3 nm and aspect ratio mainly between 1 and 1.5. Magnetic measurements indicated a superparamagnetic behavior. XRD diffractograms allowed a size estimation of 4 nm, which was associated with the nanoplate thickness. The silver-decorated zinc/calcium ferrite nanoparticles were successfully employed in the photodegradation of a model dye (Rhodamine B) and industrial textile dyes (CI Reactive Red 195, CI Reactive Blue 250 and CI Reactive Yellow 145). The nanosystems developed exhibited promising results for industrial application in effluent photoremediation using visible light, with the possibility of magnetic recovery.