TítuloEstudo de defeitos na indústria têxtil
Outro(s) título(s)Study of defects in the textile industry
Autor(es)Gonçalves, Ana Sofia da Silva
Orientador(es)Souto, A. Pedro
Rocha, A. M.
Palavras-chaveDefeito
Indústria têxtil
Controlo de qualidade
Estamparia
Acessórios metálicos
Defect
Textile industry
Quality control
Stamping
Metal accessorries
Data9-Mar-2022
Resumo(s)Um dos grandes problemas da indústria têxtil, passa pela existência de uma elevada quantidade de defeitos que podem surgir ao longo das produções. Por isso mesmo, é importante realizar estudos pormenorizados de defeitos e para se descobrir a causa, ajudando as empresas a direcionarem as suas produções para uma minimização de defeitos através de conhecimento e da forma que devem proceder quando estes aparecem ou, preferencialmente, precaverem a ocorrência de defeitos. Nesta dissertação apresenta-se o estudo de caso de três defeitos (A, B e C), com origens e causas distintas, que ocorreram na indústria têxtil. Os defeitos estudados foram problemas litigiosos entre empresas do setor têxtil, razão pela qual neste trabalho, não vai ser mencionado o nome. A abordagem adotada inclui, a análise do defeito presente na peça rececionada e, sempre que possível, a reprodução do defeito laboratorialmente. No estudo de caso do defeito A, analisou-se um estampado por sublimação que se apresentava pouco uniforme e com cores esbatidas. No estudo de caso do defeito B, examinou-se o aparecimento de uma mancha, na zona de aplicação de elementos metálicos designados de “Buckles”, em macacões infantis tingidos. No estudo de caso do defeito C, estudou-se um estampado direto aplicado em dois tipos de malhas (t-shirts e sweats) que apresentava quebras em várias cores. Com esta dissertação pretende-se aprofundar o conhecimento sobre as causas de alguns defeitos e mostrar de que forma devem ser analisados e prevenidos por parte das empresas deste setor. Sendo este um problema que é muito comum nesta indústria é importante que se conheçam as causas dos mesmos para que não voltem a acontecer em futuras produções.
One of the major problems of the textile industry is the existence of a high amount of defects that can occur during the production. For this reason, it is important to carry out detailed studies of defects to discover the cause, helping companies to direct their production towards a minimization of defects through knowledge of the way to proceed when they occur or, preferably, prevent the occurrence of defects. This dissertation presents the case study of three defects (A, B and C), with different origins and causes, which occurred in the textile industry. The defects studied are based on litigious problems between companies in the textile sector, which is why the names of the companies involved will not be mentioned in this work. The approach adopted includes analyzing the defect present in the sample received and, whenever possible, reproducing the defect in the laboratory. In the case study of defect A, we analyzed a print by sublimation that was not very uniform and had faded colors. In the case study of defect B, the appearance of a stain in the area of application of metallic elements called “Buckles” in dyed children's overalls was examined. In the case study of defect C, a direct print applied to two types of knits (t-shirts and sweats) that showed breaks in several colors was studied. This dissertation intends to deepen the knowledge about the causes of some defects and show how they should be analyzed and prevented by companies in this sector. Since this is a problem that is very common in this industry, it is important that the causes are well known so that they can be prevented in future productions.
TipoDissertação de mestrado
DescriçãoDissertação de mestrado integrado em Engenharia Têxtil
URIhttps://hdl.handle.net/1822/83758
AcessoAcesso aberto
Aparece nas coleções:BUM - Dissertações de Mestrado
DET/2C2T - Dissertações de mestrado

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
Ana Sofia da Silva Goncalves.pdf6,37 MBAdobe PDFVer/Abrir

Este trabalho está licenciado sob uma Licença Creative Commons Creative Commons

Partilhe no FacebookPartilhe no TwitterPartilhe no DeliciousPartilhe no LinkedInPartilhe no DiggAdicionar ao Google BookmarksPartilhe no MySpacePartilhe no Orkut
Exporte no formato BibTex mendeley Exporte no formato Endnote Adicione ao seu ORCID