Enzymatic surface hydrolysis of PET enhances bonding in PVC coating

Abstract

The effect of polyesterase preparations from Thermomyces lanuginosus and Beauveria brongniartii on the hydrophilicity of PET materials was assessed. As a result of polyesterase treatment the hydrophilicity of PET fabrics was increased by up to 8 cm in terms of rising height with increases in surface tension from 6.2 mNm (heat-inactivated control samples) to above 8 mNm. Both enzymes were able to increase the amount of hydroxyl groups on PET from 90 to a maximum of 182 mmol kg-1, while only the B. brongniartii polyesterase released significant amounts of terephthalic acid from PET. Enzymatic surface hydrolysis of PET increased the bonding strength in PVC coating to 13.40 daN 5cm-1 using 0.5% adhesive compared to 11.5 daN 5cm-1 obtained without enzyme pretreatment and 6% of adhesive.