Título: | Estudo de soluções de baixo impacto ambiental para revestimento têxtil |
Outro(s) título(s): | Study of low environmental impact solutions for textile coating |
Autor(es): | Vasconcelos, Joana Vinagre de Basto Vale e |
Orientador(es): | Duarte, F. M. Barroso, Eva |
Data: | 2013 |
Resumo(s): | Normalmente todas as telas ou lonas utilizadas em impressão digital consistem numa
tela de poliéster revestida com um plastisol de PVC. A utilização crescente em painéis
publicitários destes materiais associada a um tempo útil de serviço curto (algumas semanas no
caso de eventos), origina um volume significativo de telas em fim de vida, as quais tem como
principal destino os aterros. A crescente preocupação com as questões ambientais tem vindo a
desenvolver a necessidade de encontrar novos materiais compatíveis com a tecnologia já
existente utilizada no processo de revestimento, que sejam competitivos em termos de custo a
nível de mercado e que provoquem menor poluição nos aterros. Para tal neste trabalho foram
aplicados novos materiais, como os polímeros biodegradáveis, de modo a diminuir a
percentagem de material sintético num revestimento (misturas de acrílico e amido) ou a produzir
misturas com polímeros em que ambos tenham uma elevada taxa de degradação (misturas de
PVOH e amido).Este trabalho está assente em duas vertentes práticas. A primeira visa produzir
soluções ecológicas a partir das quais são fabricados filmes a fim de estudar as propriedades
mecânicas dos mesmos e caracterizar reologicamente as soluções que tem maior potencial para
revestir um suporte têxtil. A segunda parte diz respeito a um estudo de degradação realizado
num meio de compostagem em que a maioria das amostras em estudo são pequenos suportes
têxteis de PLA revestidos com uma solução à base de acrílico e amido e as restantes para
termos comparativos têm o revestimento unicamente à base de acrílico, amido ou o
revestimento é composto por uma mistura de álcool polivinílico e amido. De um modo geral a
maioria dos filmes obtidos a partir das soluções ecológicas são frágeis e quebradiços. As
soluções escolhidas têm um comportamento reofluidificante quando ocorre um aumento da taxa
de corte no campo de fluxo e as soluções que já apresentavam à temperatura ambiente uma
estrutura molecular semelhante à de um gel não apresentam um ponto de gelificação indicativo
da transição de um fluido viscoso para um solido elástico com o aumento da temperatura.
Relativamente ao estudo de degradação verificou-se que a degradação existente ocorre
principalmente na superfície do lado do revestimento para cada amostra, que a composição do
composto utilizado não é a adequada e ira degradar muito lentamente todas as amostras, que
quanto maior a quantidade de amido presente no revestimento maior é a percentagem de perda
de peso das amostras e por conseguinte este polímero biodegradável aumenta a degrabilidade
dos polímeros sintéticos. Normally all canvas used in digital printing consist of a polyester fabric coated with a PVC plastisol. The increasing use of advertising panels associated with a short service time (a few weeks in case of events), causes a significant amount of canvas at the end of life, which has as main destination landfills. The growing concern about environmental issues has developed the need to find new materials compatible with the existing technology already used in the coating process, which are competitive in terms of cost and it is expected that these cause less pollution in landfills. For this purpose, in this work were applied new materials such as biodegradable polymers , in order to decrease the percentage of synthetic material in the coating (blends of acrylic and starch) or to produce blends containing polymers where both have a high rate of degradation (blends of PVOH and starch). This work is based on two practical strands. The first aims to produce “green solutions” from which films are made in order to study their mechanical properties and to characterize rheologically the solutions that have the greatest potential for coating a textile support. The second part concerns a degradation study performed in a composting environment in which most of the samples under study are small textile supports of PLA coated with an aqueous solution of starch and acrylic and for comparative terms the others only have a coating based on acrylic, starch or the coating consists of a blend of polyvinyl alcohol and starch. In general most of the films obtained from the ecological solutions are fragile and brittle. The chosen solutions have a pseudoplastic behavior when subjected to an increasing rate of shear stress on the flow field and the solutions that already exhibited at room temperature a gel similar molecular structure don’t presente a gel point indicative of the transition of a viscous fluid to an elastic solid with increasing temperature. With regard to the degradation study, it was found that the existing degradation occurs mainly on the surface of the coating side for each sample, that the composition of the compound used is not appropriate and this will degrade very slowly all the samples. It was also found that the greater the amount of starch present in the coating the greater the percentage of weight loss of samples and therefore this biodegradable polymer increases the degradability of synthetic polymers. |
Tipo: | Dissertação de mestrado |
Descrição: | Dissertação de mestrado integrado em Engenharia de Polímeros |
URI: | https://hdl.handle.net/1822/30366 |
Acesso: | Acesso aberto |
Aparece nas coleções: | BUM - Dissertações de Mestrado DEP - Dissertações de Mestrado |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
TESE_JOANA VASCONCELOS_2013.pdf | 3,03 MB | Adobe PDF | Ver/Abrir |