Viscoelastic behaviour and time-temperature correspondence of HDPE with varying levels of process-induced orientation

dc.contributor.authorMano, J. F.eng
dc.contributor.authorSousa, R. A.eng
dc.contributor.authorReis, R. L.eng
dc.contributor.authorCunha, A. M.eng
dc.contributor.authorBevis, M. J.eng
dc.date.accessioned2003-11-11T19:11:42Z
dc.date.available2003-11-11T19:11:42Z
dc.date.issued2001
dc.description.abstractShear controlled orientation in injection moulding (SCORIM) is a non-conventional injection moulding technique that allows for the enhancement of the mechanical properties of semi-crystalline polymers. In this work the flexural mechanical feature, namely their time-dependance, of conventionally injection-moulded high-density polyethylene (HDPE) (PEc) and SCORIM-processed HDPE (PEs) are compared. The differences should be attributed to the appearance of highly oriented structures such as shish-kebab morphologies in the latter case. The quasi-static performance of HDPE shows a 59% increase in the flexural modulus following SCORIM application. Master curves of the frequency-dependence of the storage modulus and of the time-dependence of strain were constructed successfully in the region of the x-radiation. The viscoelastic data are well described by the colo-cole model. The wide broadness of the distribution of relaxation time observed for both materials is ascribed to the molecular mobility of the amorphous phase involved in the relaxation process. Two approaches were used to investigate the curvature observed in the Arrhenious plots. In the first case, two separate processes were assumed to contribut to the x-relaxation, with activation energies of 150-170 and 180-210 kj mol -1, respectively (dynamic data). However, the two x- processes, xI and xII, often reported in the literature, did not appear explicitly in the original data, which showed a single peak in an E” vs T plot. Therefore, a unique process for the x-relaxation was also assumed and was well described taking into account changes in the reduced volume whose temperature-dependence obeys a general equation of state. This concept enable a good agreement between creep and dynamic experiment.eng
dc.distributioninternationaleng
dc.identifier.citation"Polymer". 42 (2001) 6187-6198.
dc.identifier.doi10.1016/S0032-3861(01)00090-8por
dc.identifier.issn0032-3861por
dc.identifier.urihttps://hdl.handle.net/1822/278
dc.language.isoengpor
dc.peerreviewedyeseng
dc.publisherElsevier
dc.rightsrestrictedAccesseng
dc.subjectPolyethyleneeng
dc.subjectOrientationeng
dc.subjectRelaxationeng
dc.subject.wosScience & Technologypor
dc.titleViscoelastic behaviour and time-temperature correspondence of HDPE with varying levels of process-induced orientationeng
dc.typearticlepor
dspace.entity.typePublicationen
oaire.citationEndPage6198por
oaire.citationIssue14por
oaire.citationStartPage6187por
oaire.citationVolume42por
sdum.journalPolymerpor

Ficheiros

Pacote original

A mostrar 1 - 1 de 1
A carregar...
Nome:
viscoelesticpolymer.pdf
Tamanho:
709.88 KB
Formato:
Adobe Portable Document Format