Electrochromic device composed of a Di-Urethanesil electrolyte incorporating lithium triflate and 1-Butyl-3-Methylimidazolium chloride

Abstract

A di-urethane cross-linked poly(oxyethylene)/silica hybrid matrix [di-urethanesil, d-Ut(600)], synthesized by the sol-gel process, was doped with lithium triflate (LiCF3SO3) and the 1-butyl-3-methylimidazolium chloride ([Bmim]Cl) ionic liquid. The as-produced xerogel film is amorphous, transparent, flexible, homogeneous, hydrophilic, and has low nanoscale surface roughness. It exhibits an ionic conductivity of 3.64 x 10(-6) and 5.00 x 10(-4) S cm(-1) at 21 and 100 degrees C, respectively. This material was successfully tested as electrolyte in an electrochromic device (ECD) with the glass/ITO/a-WO3/d-Ut(600)(10)LiCF3SO3[Bmim]Cl/c-NiO/ITO/glass configuration, where a-WO3 and c-NiO stand for amorphous tungsten oxide and crystalline nickel oxide, respectively. The device demonstrated attractive electro-optical performance: fast response times (1-2 s for coloring and 50 s for bleaching), good optical memory [loss of transmittance (T) of only 41% after 3 months, at 555 nm], four mode modulation [bright mode (+3.0 V, T = 77% at 555 nm), semi-bright mode (-1.0 V, T = 60% at 555 nm), dark mode (-1.5 V, T = 38 % at 555 nm), and very dark mode (-2.0 V, T = 11% and -2.5 V, T = 7% at 555 nm)], excellent cycling stability denoting improvement with time, and high coloration efficiency [CEin = -6727 cm(2) C-1 (32th cycle) and CEout = +2794 cm(2) C-1 (480th cycle), at 555 nm].